HiNNY TN2098

Revolutionary Barrier Properties • Glass Fiber on Surface Elimination • Multi-Industry Versatility• Reduce water absorption

Keywords：

HiNNY TN2098

Category：

Semi-aromatic barrier nylon

Hotline：

+86 536-3371377

Contact

Inquiry

HiNNY TN2098

Details

HINNY TN2098 is a semi-aromatic transparent high barrier nylon. Due to its molecular main chain contains both aromatic ring and aliphatic chain, TN2098 has both advantages of aromatic nylon’s excellent performance and aliphatic nylon’s good molding processing.
Providing an excellent oxygen and water barrier properties, as well as excellent tolerance to solvents.

Generally has the advantages
▪ High temperature resistance, corrosion resistance.
▪ Low water absorption
▪ High hardness and transparency
▪ Excellent solvent resistance
▪ High barrier property to oxidation and water

APPLICATION
1.Automotive transparent container, oil cistern

2. Polyamide barrier film for flexible packaging, include food barrier film, cosmetic packaging
3.Used in PA6/PA66 with glass fiber compound systems to:
• Eliminate Glass Fiber on Surface
• Reduce water absorption & warping
• Improve material properties

Product parameters

Basic Information	TN2098	Unit	Test method
Resin identification	PA		ISO1043
Identification code	>PA<		ISO11469
Physical Property
Density	1.18	g/cm³	ISO1183
Water absorption	5	%	ISO62
Transmittance	≥85	%
Contraction rate parallel	0.6	%	ISO294-4,2577
Vertical	0.7	%	ISO294-4,2577
Mechanical properties
Tensile strength	90	MPa	ISO527-1/-2
Tensile modulus	2850	MPa	ISO527-1/-2
Elongation rate at break	50	%	ISO527-1/-2
Bending modulus	3100	MPa	ISO178
Bending strength	120	MPa	ISO178
Charpy Notched Impact Strength	9	KJ/㎡	ISO179/1eU
Thermal performance
Melt Index	4	g/min	ISO11357-1/-3
Thermal deformation temperature(1.8MPa)	110	°C	ISO75-1/-2
Thermal deformation temperature(0.45MPa)	125	°C	ISO75-1/-2
Combustibility
Combustion grade	HB	class	UL94

Pre